High-tonnage flexible ultra-high molecular weight polyethylene (UHMWPE) sling lifting belt, marine-grade circular eye, custom 10-3000T tonnage
Specification
| UHMWPE Endless Sling Webbing | ||||||||||
| Load Capacity（T) | 10 | 20 | 30 | 40 | 30 | 60 | 80 | 100 | 200 | 400 |
| Diameter(mm） | 28 | 35 | 45 | 50 | 58 | 62 | 68 | 75 | 100 | 180 |
| Length（m) | Custom Length: 1 - 100 m | |||||||||
| Note:Dimensions are manually measured and for reference only. | ||||||||||
| UHMWPE Sling Webbing with Eye | ||||||||||
| Load Capacity（T) | 10 | 15 | 20 | 30 | 40 | 50 | 60 | 70 | 80 | 100 |
| Diameter(mm） | 38 | 45 | 55 | 65 | 73 | 80 | 85 | 90 | 95 | 105 |
| Length（m) | Custom Length: 1 - 100 m | |||||||||
Why Choose Ultra-High Molecular Weight Polyethylene Fiber?
Ultra-High Molecular Weight Polyethylene Fiber (abbreviated as UHMWPE or PE fiber) is a high-performance synthetic fiber with unique physical and chemical properties. It is widely used in military, aerospace, marine engineering, medical and sports equipment, and other fields.
1）Physical Properties:Melting Point: 135°C–145°C、Electrical Resistance: 10^14 Ω、Boiling Water Shrinkage: <1%、Thermal Conductivity: 20 W/(m·K)
2）Chemical Resistance:No performance degradation after 6 months of immersion in：Distilled water, seawater, kerosene, 100% detergent, gasoline, hydrochloric acid, glacial acetic acid, toluene, sodium hydroxide, ammonium hydroxide.
3）Weathering Resistance:After 1500 hours of continuous UV exposure, the strength retention rate remains above 90%, whereas other chemical fibers typically show retention rates around 40% or lower.
4）Tension Fatigue Performance:After thousands of cyclic loading tests, the fiber retains nearly full strength, demonstrating excellent tension fatigue resistance.
5）Abrasion & Flex Resistance:Abrasion Resistance: >110 × 10³ times、Flex Resistance: >240 × 10³ times、Loop & Knot Strength: 10–15 times、Loop Formation Strength: 12–18 times
6）Mechanical Properties:Density: 0.97 g/cm³ (lower than water, enabling flotation)、Strength: 35–40 G/D、Modulus: 1000–1500G/D、Elongation at Break: 3.5%